Material Notes:

10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.

 

 

Physical Properties

Metric

English

Comments

Specific Gravity 

1.34 g/cc

1.34 g/cc

ASTM D792

Melt Flow 

11.3 g/10 min
@Load 6.60 kg,
Temperature 337 °C

11.3 g/10 min
@Load 14.6 lb,
Temperature 639 °F

ASTM D1238

Mechanical Properties

Metric

English

Comments

Tensile Strength at Break 

115 MPa

16700 psi

Type I, 5 mm/min; ASTM D638

Tensile Strength, Yield 

114 MPa

16500 psi

Type I, 5 mm/min; ASTM D638

Elongation at Break 

6.00 %

6.00 %

Type I, 5 mm/min; ASTM D638

Tensile Modulus 

4.61 GPa

669 ksi

5 mm/min; ASTM D638

Flexural Strength 

199 MPa

28900 psi

brk, 2.6 mm/min, 100 mm span; ASTM D790

Flexural Modulus 

5.24 GPa

760 ksi

2.6 mm/min, 100 mm span; ASTM D790

Izod Impact, Notched 

0.480 J/cm

0.899 ft-lb/in

ASTM D256

 

4.00 J/cm
@Thickness 3.20 mm

7.49 ft-lb/in
@Thickness 0.126 in

ASTM D256

Electrical Properties

Metric

English

Comments

Arc Resistance 

60.0 - 120 sec

60.0 - 120 sec

Tungsten; ASTM D495

Comparative Tracking Index 

100 - 175 V

100 - 175 V

UL 746A

Hot Wire Ignition, HWI 

60.0 - 120 sec

60.0 - 120 sec

UL 746A

High Amp Arc Ignition, HAI 

0.000 - 15.0 arcs

0.000 - 15.0 arcs

UL 746A

High Voltage Arc-Tracking Rate, HVTR 

25.4 - 80.0 mm/min

1.00 - 3.15 in/min

UL 746A

Thermal Properties

Metric

English

Comments

Deflection Temperature at 1.8 MPa (264 psi) 

207 °C
@Thickness 6.40 mm

405 °F
@Thickness 0.252 in

unannealed; ASTM D648

UL RTI, Electrical 

170 °C

338 °F

UL 746B

UL RTI, Mechanical with Impact 

170 °C

338 °F

UL 746B

UL RTI, Mechanical without Impact 

170 °C

338 °F

UL 746B

Flammability, UL94  

V-0
@Thickness 0.400 mm

V-0
@Thickness 0.0157 in

UL 94

 

5VA
@Thickness 1.90 mm

5VA
@Thickness 0.0748 in

UL 94